Thermal Fatigue Behavior of Nitrocarburized and Low Pressure Nitrided Modified JIS SKD61 Hot Work Mold Steel
-
- Yeh Shu-Hung
- Department of Materials Engineering, Tatung University
-
- Chiu Liu-Ho
- Department of Materials Engineering, Tatung University
-
- Lo Wan-Chung
- Metal Industries Research & Development Centre
-
- Huang Chien-Lung
- Metal Industries Research & Development Centre
この論文をさがす
抄録
A novel method using induction heating equipment was employed to investigate the thermal fatigue behaviors of two hot-work steels, JIS SKD61 and modified JIS SKD61, vacuum hardened treated to 45 HRC. Selected specimens, austenitized at 1298 K for 25 min, gas quenched to room temperature and tempered at 873 K, were salt bath nitrocarburized at 843 K for 80 min and low pressure nitrided at 813 K for 6 h, respectively. Microstructure, microhardness, X-ray diffraction and thermal fatigue tests were conducted. The results show that the thermal fatigue properties of the 898 K tempered specimen were better than those of other treated specimens. The reason is that the hardened processes would give high tensile strength, which improved the tool material thermal fatigue resistance. The thermal fatigue properties of modified JIS SKD61 specimen, including mean crack length and crack distribution density, were better than those of JIS SKD61 specimen. Low pressure nitriding treatment with a homogeneous nitrided layer could better maintain thermal fatigue resistance than the nitrocarburized steel.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 54 (7), 1187-1194, 2013
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249657728
-
- NII論文ID
- 10031183667
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3sXhsVGjt77I
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 024647638
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可