Composition-Dependent Thermoelectric Properties of (PbTe)100-x(Bi2Te3-Sb2Te3)x(0.1≦x≦5)
-
- Zhu Pinwen
- Eco-material Research Center, National Institute for Materials Science National Lab of Superhard Materials, Jilin University
-
- Imai Yoshio
- Eco-material Research Center, National Institute for Materials Science
-
- Isoda Yukihiro
- Eco-material Research Center, National Institute for Materials Science
-
- Shinohara Yoshikazi
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
- Jia Xiaopeng
- National Lab of Superhard Materials, Jilin University
-
- Zou Guangtian
- National Lab of Superhard Materials, Jilin University
書誌事項
- タイトル別名
-
- Composition-Dependent Thermoelectric Properties of (PbTe)<SUB>100−<I>x</I></SUB>(Bi<SUB>2</SUB>Te<SUB>3</SUB>-Sb<SUB>2</SUB>Te<SUB>3</SUB>)<I><SUB>x</SUB></I> (0.1<I>≤x≤</I>5)
- Composition Dependent Thermoelectric Properties of PbTe 100 x Bi2Te3 Sb2Te3 x 0 1 x 5
- Composition-Dependent Thermoelectric Properties of (PbTe)<SUB>100−<I>x</I></SUB>(Bi<SUB>2</SUB>Te<SUB>3</SUB>-Sb<SUB>2</SUB>Te<SUB>3</SUB>)<I><SUB>x</SUB></I> (0.1<I>≤x≤</I>5)
この論文をさがす
説明
We report room-temperature thermoelectric properties of polycrystalline (PbTe)100−x(Bi2Te3-Sb2Te3)x (0.1≤x≤5). At x≤0.25, with a decrease of x, the electrical resistivity increases dramatically whereas the Seebeck coefficient and the thermal conductivity nearly keep constant. At x≥0.5, the electrical conductivity, the thermal conductivity and the Seebeck coefficient in absolute value slightly decrease with increasing x. It is found that, the thermal conductivity of the PbTe sample with Bi2Te3 and Sb2Te3 as the sources of dopants is much smaller than that of doping with other dopants at the same carrier concentration. With an increase of x, the figure of merit, Z, which is calculated from the measured quantities, increases at first and then decreases and shows a maximum value of 8.97×10−4 K−1 at x=0.2. This value is several times higher than that of small grain-size PbTe containing other dopants.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (4), 761-764, 2005
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249781632
-
- NII論文ID
- 130004452763
- 10015520465
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2MXlt1yit70%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7304330
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可