Influence of Substrate Temperature on Structure and Adhesion Strength of Fe–Cr–P–C Amorphous Coating Films Produced by Thermal Spraying Technique
-
- Komaki Masahiro
- Nakayama Steel Works, Ltd., R&D Division
-
- Mimura Tsunehiro
- Nakayama Steel Works, Ltd., R&D Division
-
- Kurahasi Ryurou
- Nakayama Steel Works, Ltd., R&D Division
-
- Odahara Hirotaka
- Institute for Materials Research, Kansai Center, Tohoku University
-
- Amiya Kenji
- Institute for Materials Research, Kansai Center, Tohoku University
-
- Saotome Yasunori
- Institute for Materials Research, Kansai Center, Tohoku University
-
- Yamasaki Tohru
- University of Hyogo
書誌事項
- タイトル別名
-
- Influence of Substrate Temperature on Structure and Adhesion Strength of Fe–Cr–P–C Amorphous Coating Films Produced by Thermal Spraying Technique
この論文をさがす
抄録
The influence of the substrate temperature on the structure, the pore distribution, and the adhesion strength of Fe-10Cr-based amorphous coating films has been examined. The amorphous coating films have been produced by a thermal spraying technique using our developed cylindrical nozzle on SS400 substrates. The splat morphology of the sprayed particles changed drastically from an irregular splash shape to a disk shape at a transition temperature of about 325°C. When the substrate temperature increased to the transition temperature region, between 325 and 350°C, the porosity in the boundary regions between the sprayed coating films and the substrates drastically decreased to about 6%, which may be due to the drastic increase in the wettability of the sprayed particles accompanied with the change of morphology from the splashed shape to the disk shape. When the substrate temperature increased from the transition temperature of 325°C up to 400°C, the porosity decreased gradually, and the volume fraction of the amorphous phase increased with increasing substrate temperature, resulting in an increase in the adhesion strength up to about 15 MPa.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 53 (4), 681-689, 2012
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204249829760
-
- NII論文ID
- 10030550751
- 130004694436
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC38XnsVKht74%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 023535999
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可