Effect of Hydrogen Absorption on Electrical Transport Properties for Ni₃₆Nb₂₄Zr₄₀ Amorphous Alloy Ribbons
-
- Umetsu Rie Y.
- Institute for Materials Research, Tohoku University
-
- Yoshida Hajime
- Research Institute for Electromagnetic Materials
-
- Fukuhara Mikio
- Research Institute for Electromagnetic Materials
-
- Yamaura Shin-ichi
- Institute for Materials Research, Tohoku University
-
- Matsuura Makoto
- Institute for Materials Research, Tohoku University
-
- Sasaki Toshio
- Institute for Materials Research, Tohoku University Institute for Nanoscience & Nanotechnology, Waseda University
-
- Sekiguchi Tetsushi
- Institute for Nanoscience & Nanotechnology, Waseda University
-
- Saito Mikiko
- Institute for Nanoscience & Nanotechnology, Waseda University
-
- Mizuno Jun
- Institute for Nanoscience & Nanotechnology, Waseda University
-
- Kawarada Hiroshi
- Institute for Nanoscience & Nanotechnology, Waseda University
書誌事項
- タイトル別名
-
- Effect of Hydrogen Absorption on Electrical Transport Properties for Ni<sub>36</sub>Nb<sub>24</sub>Zr<sub>40</sub> Amorphous Alloy Ribbons
この論文をさがす
抄録
Electrical resistivity measurements in the temperature range from 6 to 300 K were carried out in order to investigate the effects of the hydrogen absorption on the transport properties of Ni36Nb24Zr40 amorphous alloy ribbon. The electrical resistivity basically behaved negative temperature dependence in all prepared specimens of (Ni0.36Nb0.24Zr0.40)100−xHx with 0 ≤ x < 15. The absolute value of temperature coefficient of the resistivity, TCR, increased with increasing the amount of the absorbed hydrogen. In addition, it was also clear that the electrical resistivity gradually increased with the time just after electrochemically charging, and tended to saturate after about 800 ks at 300 K. The behavior of the gradual increase in the electrical resistivity with the time was explained by the model including two kinds of the relaxation times, being associated with the migration of the hydrogen from the sample surface.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 54 (8), 1339-1342, 2013
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249881344
-
- NII論文ID
- 10031189485
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3sXhs1Sqtb7I
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 024716268
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可