Development of Ni-Pd-P-B Bulk Metallic Glasses with High Glass-Forming Ability
-
- Yuqiao Zeng
- Institute for Materials Research, Tohoku University
-
- Nishiyama Nobuyuki
- R&D Institute of Metals and Composites for Future Industries (RIMCOF)
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
この論文をさがす
抄録
A small amount of boron was added to Ni60Pd20P20 and Ni65Pd15P20 alloys. The alloys containing 3 at% boron showed improved thermal stability and glass-forming ability. The supercooled liquid region of as-spun ribbons was enlarged by about 10 K for both Ni60Pd20P17B3 and Ni65Pd15P17B3 alloys. The critical diameters for glass formation were increased up to 15 mm for Ni60Pd20P17B3 and 10 mm for Ni65Pd15P17B3, respectively. The reason of the minor B addition leading to the significant improvements of thermal stability and glass-forming ability was investigated.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 50 (6), 1243-1246, 2009
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249903360
-
- NII論文ID
- 10024815405
- 130004454250
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 10236764
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可