Notched Tensile Fracture of Ti–6Al–4V Laser Welds at Elevated Temperatures
-
- Lu M. Y.
- Institute of Materials Engineering, National Taiwan Ocean University
-
- Tsay L. W.
- Institute of Materials Engineering, National Taiwan Ocean University
-
- Chen C.
- Department of Material Science and Engineering, National Taiwan University
書誌事項
- タイトル別名
-
- Notched Tensile Fracture of Ti–6Al–4V Laser Welds at Elevated Temperatures
この論文をさがす
抄録
Notched tensile tests of Ti–6Al–4V laser welds that were subjected to post-weld heat treatments (PWHTs) at 482 and 704°C were carried out in air at temperatures from 25 to 450°C. The experimental results were also compared with those of the mill-annealed base metal (MB) specimens tested at similar temperatures. Generally, the notched tensile strength (NTS) of the specimens was sensitive to the test temperature. The NTS of laser welds was lower than that of the MB specimen at room temperature, but the trend reversed at 450°C. The presence of thick grain boundary α layers, which promoted intergranular fracture at elevated temperatures, could account for the lowered NTS of the weld after PWHT at 704°C.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 53 (6), 1042-1047, 2012
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249995904
-
- NII論文ID
- 10030629984
- 130004824874
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 023682100
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可