Mechanical behavior of Ti3AlC2 prepared by pulse discharge sintering method
-
- Zou Yong
- Materials Research Institute for Sustainable Development, National Institute of Advanced Industrial Science and Technology (AIST) Institute of Thermal Science and Technology, Shandong University
-
- Sun ZhengMing
- Materials Research Institute for Sustainable Development, National Institute of Advanced Industrial Science and Technology (AIST)
-
- Hashimoto Hitoshi
- Materials Research Institute for Sustainable Development, National Institute of Advanced Industrial Science and Technology (AIST)
-
- Tada Shuji
- Materials Research Institute for Sustainable Development, National Institute of Advanced Industrial Science and Technology (AIST)
書誌事項
- タイトル別名
-
- Mechanical Behavior of Ti<SUB>3</SUB>AlC<SUB>2</SUB> Prepared by Pulse Discharge Sintering Method
この論文をさがす
抄録
Almost single-phase ternary compound Ti3AlC2 was successfully synthesized by pulse discharge sintering (PDS) from Ti/Al/TiC powder mixtures with molar ratio of 2:2:3. The typical microstructure of Ti3AlC2 was found to consist of plate-like grains with mean size of 9.5 μm in length. Four-point bending testing results revealed that the fracture behavior is brittle below 1200°C, and some characteristics of plastic deformation were observed at higher testing temperatures. The polycrystalline Ti3AlC2 synthesized by PDS technique shows good strength at high temperatures.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (9), 2432-2435, 2007
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204250049152
-
- NII論文ID
- 10019853761
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8885280
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可