Effects of shaping conditions on the microstructure and the mechanical property of the Al2O3-YAG eutectic composite produced by melting the Al2O3-YAP eutectic structure
書誌事項
- タイトル別名
-
- Effects of Shaping Conditions on the Microstructure and the Mechanical Property of the Al<SUB>2</SUB>O<SUB>3</SUB>-YAG Eutectic Composite Produced by Melting the Al<SUB>2</SUB>O<SUB>3</SUB>-YAP Eutectic Structure
この論文をさがす
抄録
When the Al2O3-YAP metastable eutectic system was heated above the metastable eutectic temperature but below the equilibrium eutectic temperature, undercooled melt was formed. Solidification in the equilibrium path accompanied the melting of the metastable eutectic system, resulting in a fine and uniform eutectic structure. A novel solidification process using undercooled melt formation was developed. In this paper, the influences of the initial Al2O3-YAP eutectic particle size, forming pressure and holding time at the maximum temperature on the microstructure and/or the mechanical property of the Al2O3-YAG compact were examined to optimize the forming conditions. The Al2O3-YAG compact produced from the Al2O3-YAP eutectic particles with diameters less than 20 μm exhibited a higher flexural strength and the smaller porosity as compared to that produced from Al2O3-YAP eutectic particles with diameters ranging from 20 μm to 45 μm. The volume fraction of the porosity was approximately 4% under a forming pressure of 10 MPa and a holding time of 60 s. The flexural strength of the Al2O3-YAG compact decreased with the increase in the holding time due to the increase in the lamellar spacing. For Al2O3-YAP eutectic particles with diameters less than 20 μm, a low forming pressure of 10 MPa and a short holding time of 60 s were sufficient to synthesize a dense Al2O3-YAG compact. Thus, the solidification technique that uses undercooled melt produced by melting the Al2O3-YAP metastable eutectic system has good advantages for shaping.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (9), 2312-2315, 2007
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204250065280
-
- NII論文ID
- 10019853205
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8884674
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可