Joints of Cf/SiC Composite to Ti-Alloy with In-Situ Synthesized TiCx Improved Brazing Layers
-
- Lin Guobiao
- School of Materials Science and Engineering, University of Science and Technology Beijing
-
- Huang Jihua
- School of Materials Science and Engineering, University of Science and Technology Beijing
-
- Zhang Huang
- School of Materials Science and Engineering, University of Science and Technology Beijing
-
- Zhao Xingke
- School of Materials Science and Engineering, University of Science and Technology Beijing
書誌事項
- タイトル別名
-
- Joints of Cf/SiC Composite to Ti-Alloy with <I>In-Situ</I> Synthesized TiC<I><SUB>x</SUB></I> Improved Brazing Layers
この論文をさがす
抄録
Cf/SiC composite was brazed to Ti-alloy by using interlayer of Ag-Cu-Ti-C mixed powder. Microstructure and both the room temperature and 500°C shear strengths of the brazed joint were investigated. In situ synthesized TiCx (x≤1) is formed in the brazing layer of the joint by the reaction of C and Ti in the brazing layers and provides good reinforcement and alleviation of the joint thermal stress.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (4), 1261-1263, 2006
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250386560
-
- NII論文ID
- 10017413178
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7887317
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可