Effect of Copper Addition on the Active Corrosion Behavior of Hyper Duplex Stainless Steels in Sulfuric Acid
-
- Lee Jun-Seob
- Department of Materials Science and Engineering, Yonsei University
-
- Kim Soon-Tae
- Department of Materials Science and Engineering, Yonsei University
-
- Lee In-Sung
- Department of Materials Science and Engineering, Yonsei University
-
- Kim Gwang-Tae
- Stainless Steel Research Group, POSCO Technical Research Laboratories
-
- Kim Ji-Soo
- Stainless Steel Research Group, POSCO Technical Research Laboratories
-
- Park Yong-Soo
- Department of Materials Science and Engineering, Yonsei University
この論文をさがす
抄録
The effect of copper (Cu) addition on the active corrosion behavior of hyper duplex stainless steels in sulfuric acid was investigated. The addition of Cu in the base alloy enhanced the resistance to general corrosion by decreasing the critical and corrosion current densities, and increasing the polarization resistance. There are two primary reasons for the considerable enhancement of the corrosion resistance of the experimental alloys containing Cu. First, the protective surface film was enriched with the noble metallic copper (Cu) due to the selective dissolution of the active metallic Cr, Fe, and Ni, and the electrochemical dissolution of the corrosion products such as iron-sulfide (FeS2), iron sulfate (FeSO4), ferrous oxide (FeO) and hydrous iron sulfate (FeSO4·7H2O). Second, chromium oxide (Cr2O3), chromium trioxide (CrO3), nickel oxide (NiO), molybdenum dioxide (MoO2), molybdenum trioxide (MoO3), and tungsten trioxide (WO3) in an oxide state, molybdenum oxy-hydroxide (MoO[OH]2) and chromium hydroxide (Cr[OH]3) in a hydro-oxide state, molybdate (MoO42−) and tungstate (WO42−) as corrosion inhibitors in an ion state, and ammonium (NH4+) elevating the pH in an ion state were increased and assisted in improving the corrosion resistance.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 53 (6), 1048-1055, 2012
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250407936
-
- NII論文ID
- 10030630002
- 130004824895
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 023682118
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可