Interface Microstructure and Mechanical Properties of Dissimilar Friction Stir Welded Joints between Zr₅₅Cu₃₀Ni₅Al₁₀ Bulk Metallic Glass and Pure Al
-
- Sun Yufeng
- Joining and Welding Research Institute, Osaka University
-
- Fujii Hidetoshi
- Joining and Welding Research Institute, Osaka University
-
- Imagawa Koichi
- Joining and Welding Research Institute, Osaka University
-
- Yokoyama Yoshihiko
- Institute for Materials Research, Tohoku University
-
- Kimura Hisamichi
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Interface Microstructure and Mechanical Properties of Dissimilar Friction Stir Welded Joints between Zr<sub>55</sub>Cu<sub>30</sub>Ni<sub>5</sub>Al<sub>10</sub> Bulk Metallic Glass and Pure Al
この論文をさがす
抄録
Dissimilar friction stir welding of Zr55Cu30Ni5Al10 bulk metallic glass (BMG) to pure Al was carried out at different welding conditions. Sound BMG/Al joints can be obtained at a rotation speed of 350 and 400 rpm. However, defects or crack may form in the stir zone when the rotation speed was either too low or too high. In the sound joints, a clear and straight BMG/Al interface was formed and no intermetallic compounds caused either by chemical reaction or crystallization from the amorphous phase can be detected within the entire stir zone. The hardness of Al side in the stir zone decreases with increasing of the rotation speed and is lower than that in the base material due to frictional heat input. The sound BMG/Al joints fractured in the heat affect zone of Al side and the tensile strength can reach about 91% of that of the base material.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 53 (6), 1106-1112, 2012
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204250441216
-
- NII論文ID
- 10030630180
- 130004824888
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 023682324
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可