Ni-Rich Ni–Pd–P Glassy Alloy with High Strength and Good Ductility
-
- Zeng Yuqiao
- Institute for Materials Research, Tohoku University
-
- Nishiyama Nobuyuki
- RIMCOF Tohoku Univ. Lab., R&D Institute of Metals and Composites for Future Industries
-
- Wada Takeshi
- Institute for Materials Research, Tohoku University
-
- Louzguine-Luzgin Dmitri V.
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Ni-Rich Ni–Pd–P Glassy Alloy with High Strength and Good Ductility
この論文をさがす
抄録
We found that a Ni-rich alloy with the composition of Ni50Pd30P20 had high glass-forming ability. Bulk glassy alloy rods with diameters up to 7 mm can be easily formed by a water quenching method. Its mechanical properties were measured under compressive load. The bulk glassy alloy exhibits relatively high yield strength of 1780 MPa and good ductility as is evidenced from a large plastic elongation of 7.6% before final fracture. The elastic properties of this bulk glassy alloy were also investigated.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (1), 175-178, 2006
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204250604032
-
- NII論文ID
- 130004452917
- 10017151511
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
- http://id.crossref.org/issn/09161821
-
- NDL書誌ID
- 7773447
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可