In-Situ Synthesis of Ti Matrix Composite Reinforced with Dispersed Ti5Si3 Particles via Spark Plasma Sintering
-
- Sumida Masaki
- Research Center for Advanced Science and Technology, the University of Tokyo
-
- Kondoh Katsuyoshi
- Research Center for Advanced Science and Technology, the University of Tokyo
書誌事項
- タイトル別名
-
- <I>In-Situ</I> Synthesis of Ti Matrix Composite Reinforced with Dispersed Ti<SUB>5</SUB>Si<SUB>3</SUB> Particles via Spark Plasma Sintering
この論文をさがす
説明
In this work, Ti matrix composite reinforced with dispersed Ti5Si3 particles was synthesized via spark plasma sintering starting with Ti and SiO2. Because reports on the equilibrium phase diagram show that there is a two phase region with O dissolved Ti, Ti(O), and Ti5Si3, Ti and small amount of SiO2 transform into Ti5Si3/Ti composite according to a reaction, Ti+SiO2=Ti(O)+Ti5Si3. Initial amount of SiO2 and sintering temperature were varied in ranges of 2.5–15 mass% and 800–1200°C, respectively. Their dependence on microstructure, bulk density, fraction of spatial occupation and Vickers hardness was studied systematically. From microstructure observation, composition and temperature range to yield Ti5Si3/Ti composite was identified. At low temperature sintering, however, SiO2 remained inside the Ti5Si3 envelope, indicating incompleteness of above reaction. A simple analysis was made on the phase transformation mechanism of Ti5Si3, supposing that the diffusion of Ti controls this process. Vickers hardness of the Ti5Si3/Ti composite increases with increase both in amount of SiO2 and temperature, but it is remarkably larger than that of commercial pure Ti. The bulk density and fraction of spatial occupation also increases with increase in temperature but decreases with increase in amount of SiO2. Taking into account the experimental and analytical results, microstructure formation and its effect on the properties are discussed briefly.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (10), 2135-2141, 2005
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204250907776
-
- NII論文ID
- 130004452601
- 10018277428
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7487710
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可