Ni3Al with and without boron was melted and unidirectionally solidified in pressurized hydrogen atmosphere by using a continuous zone melting method. For Ni3Al without boron, cylindrical pores elongated in the direction parallel to the solidification direction, are formed in Ni3Al matrix. On the other hand, no pore is formed in Ni3Al with 0.23 mol% B solidified under the same condition. This result suggests that the solubility gap of hydrogen between liquid and solid Ni3Al with boron is extremaly small.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (9), 2116-2119, 2006
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250928128
-
- NII論文ID
- 130004453273
- 10018248496
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8061635
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可