Slip Morphology and Recrystallization in Copper Single Crystals Tensile-Deformed along〈011〉and〈001〉Direction
-
- Okada Tatsuya
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
-
- Utani Mitsuyoshi
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
-
- Osue Atsushi
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
-
- Fujii Nobukazu
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
-
- Tagami Minoru
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
-
- Inoko Fukuji
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
書誌事項
- タイトル別名
-
- Slip Morphology and Recrystallization in Copper Single Crystals Tensile-Deformed along ⟨011⟩ and ⟨001⟩ Direction
- Slip Morphology and Recrystallization in Copper Single Crystals Tensile Deformed along 011 and 001 Direction
- Slip Morphology and Recrystallization in Copper Single Crystals Tensile-Deformed along ⟨011⟩ and ⟨001⟩ Direction
この論文をさがす
説明
Single crystals of pure copper were tensile-deformed along ⟨011⟩- and ⟨001⟩ direction and then annealed to study their deformation and recrystallization behaviors. In the ⟨011⟩ single crystals, no large-scale deformation band was formed. The areas where the secondary slip was activated were small and were randomly distributed throughout the deformed crystals. Large rotation with respect to the initial orientation was found. After annealing, many recrystallized grains were formed. In the ⟨001⟩ single crystal, because of almost equal activation of eight slip systems on four slip planes, orientation change associated with deformation was very small. Large-scale cross-slip was completely suppressed. As a result, the work-hardening of the ⟨001⟩ single crystal was very large. After annealing, large primary recrystallized grains were formed. The above results are compared with those of aluminum single crystals having the same tensile orientations.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (3), 602-607, 2005
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204250997376
-
- NII論文ID
- 10015579148
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2MXjvFSru7Y%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7289951
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可