Characteristic Structural Changes in Stress-Induced Martensitic Transformation and Reverse Transformation of a Polycrystalline Fe-Mn-Si Alloy
-
- Suzuki Shigeru
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
- Senoo Shotaro
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
- Maruyama Tadakatsu
- Awaji Materia Co. Ltd
-
- Shinoda Kozo
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
この論文をさがす
説明
Debye rings obtained by synchrotron X-ray diffraction were analyzed for investigating structural changes caused by stress-induced martensitic transformation and reverse transformation of a polycrystalline austenitic Fe-Mn-Si shape memory alloy. The chemical composition of the shape memory alloy was Fe-28 mass%Mn-6 mass%Si-5 mass%Cr. The results showed that a part of the austenitic γ phase was transformed to a martensitic ε phase by room-temperature tensile deformation, and the ε phase was reversely transformed by subsequent heating. Diffraction intensities in Debye rings changed non-uniformly on tensile deformation and heating, indicating that occurrences of the stress-induced and reverse transformation depend on the crystallographic orientations of grains with respect to the tensile direction. The optimum recovery strain induced by the reverse transformation was obtained for a sample deformed by about 10% tensile strain, which was consistent with the structural changes caused by the reverse transformation. X-ray diffraction lines were shown to be broadened by tensile strain. This indicated that irreversible deformation due to dislocations restricted the reverse transformation, leading to the optimum recovery strain.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (12), 2755-2760, 2008
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204251014144
-
- NII論文ID
- 10024403800
- 130004453887
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9728638
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可