Study of Thermal Stability of Ultrafine-Grained Copper by means of Electron Back Scattering Diffraction

DOI Web Site Web Site 参考文献34件
  • Man Ond\\v{r}ej
    Institute of Materials Sciences and Engineering, Faculty of Mechanical Engineering, Brno University of Technology
  • Pant\\v{e}lejev Libor
    Institute of Materials Sciences and Engineering, Faculty of Mechanical Engineering, Brno University of Technology
  • Kunz Ludvík
    Institute of Physics of Materials, Academy of Sciences of Czech Republic

この論文をさがす

説明

Thermal stability of ultrafine-grained (UFG) structure of 99.9% pure copper produced by eight equal channel angular pressing (ECAP) passes was studied. The annealing experiments were conducted at 180°C in a tube furnace under argon as a covering gas. The dwell times were in the range of 10 min to 120 min. The electron backscattering diffraction (EBSD) analyses were performed before and after annealing at exactly the same area in order to quantify the degree of decomposition of the UFG structure. Definition of grain boundaries was based on the misorientation angle of 1°. More advanced analysis of the EBSD results based on a kernel average misorientation (KAM) parameter was performed. Inverse pole figure maps with included grain networks did not reveal any substantial changes of UFG microstructure due to annealing. Some shift in the KAM modus in comparison with the initial state was observed but its magnitude was found negligible. Also changes in texture were found to be minor. On the other hand the microhardness increases with increasing time of annealing.

収録刊行物

参考文献 (34)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ