Microstructure Evaluation of Friction Stir Welded AZ91 with CaO Mg Alloy
-
- Choi Don Hyun
- School of Advanced Materials Science and Engineering, Sungkyunkwan University
-
- Ahn Byung Wook
- School of Advanced Materials Science and Engineering, Sungkyunkwan University
-
- Kim Shae Kwang
- Korea Institute of Industrial Technology
-
- Yeon Yun Mo
- Department of Advanced Materials Application, Suwon Science College
-
- Kim Young Jik
- School of Advanced Materials Science and Engineering, Sungkyunkwan University
-
- Park Sun-Kyu
- School of Civil and Environmental Engineering, Sungkyunkwan University
-
- Jung Seung Boo
- School of Advanced Materials Science and Engineering, Sungkyunkwan University
この論文をさがす
抄録
The present study was carried out to evaluate the microstructural properties of a friction stir welded AZ91 with CaO Mg alloy. For this work, friction stir welding (FSW) was performed at a tool rotation speed of 1250 rpm and a traveling speed of 32 mm·min−1. A network of intermetallic compounds (Al2Ca) was observed in the base metal (BM). In the stir zone (SZ), fine grains and intermetallic compound particles were formed due to dynamic recrystalization and mechanical stirring. The hardness profile showed that the hardness of the SZ was higher than that of the BM, probably due to the presence of fine grains and thermally stable intermetallic compounds.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (4), 802-805, 2011
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204251433600
-
- NII論文ID
- 10028175652
- 130004454676
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3MXovVyqurk%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 11058406
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可