Hydriding Properties of (Mg1-xMx)Ni2 C15-Type Laves Phase Alloys
-
- Terashita Naoyoshi
- Japan Metals & Chemicals Co., Ltd.
-
- Akiba Etsuo
- National Institute of Advanced Industrial Science and Technology
書誌事項
- タイトル別名
-
- Hydriding Properties of (Mg<SUB>1−<I>x</I></SUB>M<I><SUB>x</SUB></I>)Ni<SUB>2</SUB> C15-Type Laves Phase Alloys
- Hydriding Properties of (Mg<SUB>1−<I>x</I></SUB>M<I><SUB>x</SUB></I>)Ni<SUB>2</SUB> C15-Type Laves Phase Alloys
この論文をさがす
抄録
Mg-based Laves phase alloys (Mg0.7M0.3)Ni2, where M elements were Ca, La, Ce, Pr, Nd and Gd were successfully developed. The alloys can be synthesized by a conventional induction melting and annealing method from intermetallic compounds MgNi2 and MNi2 as a source of Mg, Ni and M elements. The crystal structures of the major phases of annealed (Mg0.7M0.3)Ni2 alloys were C15-type for M=Ca and C15b-type for M=La, Ce, Pr, Nd and Gd Laves structures, respectively. In the alloys except M=Ce, hydrogenation and dehydrogenation reversibly occurred. The maximum hydrogen contents of the alloys are 1.2–1.6 mass% (H/M:0.6–0.8) under hydrogen pressure of 5 MPa at 243–273 K. As the results of measurements of p-c isotherms, in the case of the M=Pr and Nd, two step plateaus were clearly observed. After a few hydrogenation/dehydrogenation cycles, the alloys kept C15-type or C15b-type Laves structures without hydrogen-induced amorphization, disproportionation and decomposition.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (8), 1890-1893, 2006
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204251519104
-
- NII論文ID
- 130004453227
- 10019296680
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8021640
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可