Deformation and Recrystallization of Aluminum Bicrystals Having Asymmetric Tilt Grain Boundary
-
- Okada Tatsuya
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
-
- Kotaka Masashi
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
-
- Wada Tetsuya
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
-
- Tagami Minoru
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
-
- Inoko Fukuji
- Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
この論文をさがす
説明
Two types of aluminum bicrystals (Bicrystal 1 and 2) having an asymmetric tilt grain boundary were grown. In Bicrystal 1, the orientations of component grains were related to each other by 45° rotation about the normal of the wide surface of the tensile specimen. In Bicrystal 2, although the primary slip planes were symmetric about the grain boundary plane, the component grains were related to each other by 180° rotation about the tensile axis of the specimen. The specimens were deformed to a tensile strain of 0.3 and subsequently annealed. In both bicrystals, deformation bands were not formed symmetrically about the grain boundary. After annealing, no strain induced boundary migration was found. Recrystallization occurred through ⟨111⟩ rotation mechanism. These results were compared with the deformation and recrystallization in aluminum bicrystals having a symmetric tilt grain boundary.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (3), 838-844, 2006
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204251523200
-
- NII論文ID
- 130004453067
- 10017960239
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7858771
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可