Effects of T5 Treatment on the Microstructure and Mechanical Properties of Mg-8Al-2Li Alloy

  • Wang P. C.
    Department of Materials Science and Engineering, National Taiwan University
  • Lin H. C.
    Department of Materials Science and Engineering, National Taiwan University
  • Lin K. M.
    Department of Materials Science and Engineering, Feng Chia University
  • Lin M. C.
    Department of Materials Science and Engineering, National Taiwan University
  • Yeh M. T.
    Amli Co. Ltd.
  • Lin C. Y.
    Department of Environmental Engineering and Science, Feng Chia University

Search this article

Abstract

In this study, the effects of T5 treatment on the microstructure and mechanical properties of Mg-8Al-2Li specimens are investigated. The experimental results show the T5-treated Mg-8Al-2Li specimens will produce the β-Mg17Al12 and/or AlLi precipitates depending on the aging temperatures. The T5-treated Mg-8Al-2Li specimens will display an obvious precipitation strengthening, regardless of whether the precipitates are single β-Mg17Al12 phase or dual phases of AlLi and Mg17Al12. Their maximum tensile strengths can reach 355–375 MPa, which are 12–18% increment compared with that of the as-extruded specimen. Meanwhile, the T5-treated Mg-8Al-2Li specimens can still show good ductility with ∼9% elongation for specimens with their maximum strengths.

Journal

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 52 (7), 1363-1368, 2011

    The Japan Institute of Metals and Materials

References(33)*help

See more

Details 詳細情報について

Report a problem

Back to top