Characterization of Spinel-Structured Iron Oxide Nanoparticles Synthesized by Heating of α-FeOOH Platelets in Tetra-Ethylene Glycol

DOI Web Site Web Site 15 References
  • Latiff Hawa
    Institute of Applied Physics, University of Tsukuba
  • Kishimoto Mikio
    Institute of Applied Physics, University of Tsukuba
  • Horiuchi Akari
    Institute of Applied Physics, University of Tsukuba
  • Seki Atsushi
    Institute of Applied Physics, University of Tsukuba
  • Miyamoto Ryoichi
    Department of Surgery, Advanced Biomedical Applications, Graduate School of Comprehensive Human Science, University of Tsukuba
  • Yanagihara Hideto
    Institute of Applied Physics, University of Tsukuba
  • Oda Tatsuya
    Department of Surgery, Advanced Biomedical Applications, Graduate School of Comprehensive Human Science, University of Tsukuba
  • Ohkohchi Nobuhiro
    Department of Surgery, Advanced Biomedical Applications, Graduate School of Comprehensive Human Science, University of Tsukuba
  • Kita Eiji
    Institute of Applied Physics, University of Tsukuba

Bibliographic Information

Other Title
  • Characterization of Spinel-Structured Iron Oxide Nanoparticles Synthesized by Heating of α-FeOOH Platelets in Tetra-Ethylene Glycol

Search this article

Description

Fe3O4 particles were synthesized from platelet α-FeOOH particles by a liquid-phase reduction process using tetra-ethylene glycol as reduction agent, for their application in hyperthermia or thermoablation therapies that employ hysteresis-loss heating. Fe3O4 particles 60–100 nm in size were finally obtained by heating. The saturation magnetization of the obtained particles increased with the heating time to reach a maximum value of approximately 80 Am2/kg. In contrast, the coercive force of the particles was nearly constant at approximately 12–13 kA/m and was independent of the heating time. Lattice image observation of the synthesized Fe3O4 particles revealed to obtain single crystals. On the basis of experimental results, it was concluded that the single-crystal Fe3O4 particles were formed by recrystallization through the dissolution and precipitation of iron ions from α-Fe2O3 formed by the dehydration of α-FeOOH. The recrystallization of the Fe3O4 particles was promoted with increasing α-FeOOH particle content in tetra-ethylene glycol up to about 0.022 g/mL.

Journal

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 55 (5), 813-817, 2014

    The Japan Institute of Metals and Materials

References(15)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top