Effect of Si Addition on Microstructure and Mechanical Properties of Dual Two-Phase Ni₃Al and Ni₃V Intermetallic Alloys
-
- Hamada Yuki
- Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University
-
- Kaneno Yasuyuki
- Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University
-
- Takasugi Takayuki
- Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University
書誌事項
- タイトル別名
-
- Effect of Si Addition on Microstructure and Mechanical Properties of Dual Two-Phase Ni<sub>3</sub>Al and Ni<sub>3</sub>V Intermetallic Alloys
この論文をさがす
抄録
The effects of Si addition on the microstructures and mechanical properties of dual two-phase Ni3Al and Ni3V intermetallic alloys with a composition of Ni75Al9V13Nb3 (expressed by at%) were investigated, focusing on the substitution manner of Si for Ni, Al or V. Solubility limit of Si in the present microstructure was less than 2 at% Si irrespective of the substitution manner of Si for Ni, Al or V. The eutectoid microstructure in the channel region was degenerated when Si was substituted for V. Third-phase dispersions containing Nb, i.e., Ni16Si7Nb6 (G phase: D8a) were present at grain boundaries of the alloys exceeding the solubility limit. In the alloy in which Si was substituted for Ni, unit cell volume of the constituent Ni3Al phase increased while that of the constituent Ni3V phase little changed. In the alloy in which Si was substituted for Al, unit cell volumes of both phases decreased. The alloys in which Si was substituted for Al or Ni hardened while the alloy in which Si was substituted for V softened. The hardening in the former alloys was attributed to solid solution hardening due to Si substituted for solvent atoms Ni, Al and/or V while the softening in the latter alloy was attributed to the degenerated eutectoid microstructure in the channel region. Also, it was shown that the third-phase dispersions little affected hardness as well as yield strength.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 57 (5), 631-638, 2016
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204252240384
-
- NII論文ID
- 130005146673
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 027270098
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可