Evaluating Microstructure and High-Temperature Shear Behavior of Hot Extruded Al-Al₁₃Fe₄ Nanocomposite
-
- Nemati Narguess
- Center of Excellence for High Performance Materials, School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran Center for Nano-Wear, Yonsei University
-
- Emamy Masoud
- Center of Excellence for High Performance Materials, School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran
書誌事項
- タイトル別名
-
- Evaluating Microstructure and High-Temperature Shear Behavior of Hot Extruded Al-Al<sub>13</sub>Fe<sub>4</sub> Nanocomposite
この論文をさがす
説明
<p>The microstructure and mechanical properties of extruded aluminum matrix composites reinforced with novel Al13Fe4 complex metallic alloy (CMA) nano-particles were investigated. The large grained structure of the hot pressed matrix was refined after addition of Al13Fe4 CMAs, the effect being more pronounced for Al-5 mass% Al13Fe4 composite. The hot pressed specimens were subjected to uniaxial hot extrusion process (with a 9 : 1 ratio at 400°C). This had a great effect on the microstructural evolution of the composites. High-temperature shear punch test (SPT) was employed to investigate the effects of 1–10 mass% Al13Fe4 additions on the microstructure and mechanical properties of the as-extruded Al/Al13Fe4 composite. The shear behavior of the alloys was investigated in the temperature range of 25–350°C. Al-5 mass% Al13Fe4 nanocomposite had the highest shear strength among all the materials tested at high temperature (150, 250 and 350°C), mainly due to the semi-ideal dispersion of the thermally stable Al13Fe4 nano-particles, and the refined microstructure of the extruded specimen, which results in pronounced enhancement in mechanical properties. These thermally resistant particles are believed to increase the resistance of the composite against the applied shear stress in the deformation zone during the subjection of the material to SPT.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 57 (8), 1236-1245, 2016
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204253346304
-
- NII論文ID
- 130005165725
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 027512330
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可