Effect of Annealing Temperature on Microstructure and Superelastic Properties of Ti-Au-Cr-Zr Alloy
-
- Shinohara Yuri
- Precision and Intelligence Laboratory, Tokyo Institute of Technology
-
- Tahara Masaki
- Precision and Intelligence Laboratory, Tokyo Institute of Technology
-
- Inamura Tomonari
- Precision and Intelligence Laboratory, Tokyo Institute of Technology
-
- Miyazaki Shuichi
- Division of Materials Science, University of Tsukuba
-
- Hosoda Hideki
- Precision and Intelligence Laboratory, Tokyo Institute of Technology
この論文をさがす
説明
Effect of annealing temperature on microstructure and superelasticity of Ti-4Au-5Cr-8Zr (mol%) was investigated. Only β phase was observed in the specimen annealed at 1173 K, whereas the precipitation of Ti3Au, Zr33Ti40Au27 (Laves phase) and α phase occurred in the specimens annealed below 1073 K. Superelasticity was clearly observed in the specimens annealed at 1073 K and 1173 K, though it was absent in the specimens annealed at 873 K and 973 K. The maximum superelastic recovery strain was increased by the precipitation of Ti3Au in the specimen annealed at 1073 K. This is due to the increase in the critical stress for slip by the precipitation strengthening effect of Ti3Au.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 56 (3), 404-409, 2015
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204253623680
-
- NII論文ID
- 130004825270
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 026220615
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可