Damping Capacities of Ti<sub>50</sub>Ni<sub>50−</sub><i><sub>x</sub></i>Cu<i><sub>x</sub></i> Shape Memory Alloys Measured under Temperature, Strain, and Frequency Sweeps
-
- Chien Chen
- Department of Materials Science and Engineering, National Taiwan University
-
- Wu Shyi-Kaan
- Department of Materials Science and Engineering, National Taiwan University Department of Mechanical Engineering, National Taiwan University
-
- Chang Shih-Hang
- Department of Chemical and Materials Engineering, National I-Lan University
Bibliographic Information
- Other Title
-
- Damping Capacities of Ti₅₀Ni₅₀-xCu[x] Shape Memory Alloys Measured under Temperature, Strain, and Frequency Sweeps
- Damping Capacities of Ti<sub>50</sub>Ni<sub>50−</sub><i><sub>x</sub></i>Cu<i><sub>x</sub></i> Shape Memory Alloys Measured under Temperature, Strain, and Frequency Sweeps
Search this article
Abstract
The damping capacities of Ti50Ni50−xCux SMAs with x = 0∼20 at% were measured by DMA under temperature, strain and frequency sweep tests. The tan δ value exhibited at B2→B19 transformation is significantly higher than that at B2→B19′ transformation under temperature/strain sweep tests. In the strain sweep test, the tan δ value decreases as the frequency increases, but it increases as the applied strain increases. The tan δ curves of the strain sweep tests can be fitted by tan δ = Kεn with n values being close to the friction type model. Adding Cu enhances the tan δ values of both B19 martensite and B2→B19 transformation in 0.1∼10 Hz, but that of B19′ martensite is enhanced only at 10 Hz. From 0.1 Hz to 1 Hz, the decrement of the tan δ value in IFI term is greater than that in IFPT term for SMA with x ≥ 5 at%. In the frequency sweep test, the tan δ value increases as the x value increases under the same applied frequency, no matter whether the martensite is B19′ or B19.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 56 (2), 193-199, 2015
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204253686016
-
- NII Article ID
- 130004825244
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 026086082
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed