Improvement of Powder Properties and Chemical Homogeneity of Partially Alloyed Iron Powder by a Nanopowder Process
-
- Choi Joon-Phil
- Department of Metallurgy and Materials Science, Hanyang University
-
- Lee Geon-Yong
- Department of Metallurgy and Materials Science, Hanyang University
-
- Song Jun-Il
- Department of Metallurgy and Materials Science, Hanyang University
-
- Yun Joon-Chul
- Department of Metallurgy and Materials Science, Hanyang University
-
- Lee Jai-Sung
- Department of Metallurgy and Materials Science, Hanyang University
この論文をさがす
抄録
The present investigation focuses on the improvements in chemical homogeneity and related powder properties of partially alloyed Fe–1.50Cu–1.75Ni–0.50Mo powder by using a nanopowder process. The nanosized oxide powders of CuO–NiO–MoO3 were prepared by ball-milling for the alloying elements and blended with iron powders. The powder mixture was annealed in a reducing atmosphere, in order to reduce the oxide powders and thereafter partially alloyed with the iron powder. The produced powder was used to evaluate the microstructure, chemical composition, compressibility, and sinterability. It was found that the powder had a uniform distribution of alloying elements with high compositional homogeneity. The fine alloying elements were mostly located in the grooves of the iron powder surface, yielding morphological change, which effectively improved the flow, packing and compaction properties of the powder. The nanopowder process also promoted a diffusion reaction during sintering at 1200°C for 2 h with a homogeneous microstructure and chemical composition.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 55 (8), 1356-1362, 2014
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204253692928
-
- NII論文ID
- 130004825207
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 025617471
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可