Enhancement of Shape Memory Properties through Precipitation Hardening in a Ti-Rich Ti-Ni-Pd High Temperature Shape Memory Alloy
-
- Namigata Yuki
- Division of Materials Science, University of Tsukuba
-
- Hattori Yuki
- Division of Materials Science, University of Tsukuba
-
- Khan M. Imran
- Faculty of Materials and Chemical Engineering, GIK Institute of Engineering Sciences and Technology
-
- Kim Hee Young
- Division of Materials Science, University of Tsukuba
-
- Miyazaki Shuichi
- Division of Materials Science, University of Tsukuba Faculty of Materials and Chemical Engineering, GIK Institute of Engineering Sciences and Technology Foundation for Advancement of International Science
この論文をさがす
説明
Effects of aging on martensitic transformation temperature, microstructure and shape memory characteristics were investigated for Ti50Ni20Pd30 and Ti52Ni18Pd30 alloys. There was no significant change in the microstructure and transformation temperature by aging, irrespective of aging temperature, in case of the Ti50Ni20Pd30 alloy. On the other hand, fine Ti2Pd type precipitates were formed upon aging in the Ti52Ni18Pd30 alloy within the aging temperature range of 673-1073 K. The transformation temperature of the Ti52Ni18Pd30 alloy was sensitively dependent on the aging temperature. The Ti2Pd type nanoscaled precipitates were found to be very effective in enhancing the high temperature dimensional stability during shape memory cycling. Excellent shape memory properties with a large recovery strain and a small plastic strain even at 500 MPa were observed in the Ti52Ni18Pd30 alloy solution treated and aged at lower temperatures of 673 and 773 K owing to the formation of fine and dense Ti2Pd type precipitates.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 57 (3), 241-249, 2016
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204254563072
-
- NII論文ID
- 130005127302
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 027194384
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可