Anisotropy of Fracture Toughness of Stabilized Zirconia Investigated by Nano-Identation Method
-
- Ito Hideaki
- Graduate School of Environmental Studies, Tohoku University
-
- Sato Kazuhisa
- Fracture and Reliability Research Institute, Graduate School of Engineering, Tohoku University
-
- Unemoto Atsushi
- Graduate School of Environmental Studies, Tohoku University
-
- Hashimoto Shin-ichi
- Graduate School of Environmental Studies, Tohoku University
-
- Amezawa Koji
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
- Kawada Tatsuya
- Graduate School of Environmental Studies, Tohoku University
この論文をさがす
抄録
<p>Nano-indentation tests with a Vickers-type diamond tip were carried out on the {100} surface of a single crystal of 10 mol% yttria-stabilized zirconia (10YSZ), (Y2O3)0.1(ZrO2)0.9. By changing the contact angle of the indentation tip against the single crystal sample, the fracture toughness of 10YSZ was investigated as a function of the crystal orientation from <100> to <110> on the {100} surface. It was empirically shown that the fracture toughness of 10YSZ is anisotropic. The fracture toughness of 10YSZ was lowest in the direction of <100> among investigated orientations. This result suggests that mechanical failures in 10YSZ may occur preferentially along the direction of <100>.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 59 (1), 23-26, 2018
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204254895232
-
- NII論文ID
- 130006279160
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 028739677
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可