Preparation of Nafion-Ru(bpy)₃²⁺-Chitosan/Gold Nanoparticles Composite Film and Its Electrochemiluminescence Application
-
- QU Yingjuan
- School of Chemistry & Chemical Engineering, Shaanxi Normal University
-
- LIU Xiaoli
- School of Chemistry & Chemical Engineering, Shaanxi Normal University
-
- ZHENG Xingwang
- School of Chemistry & Chemical Engineering, Shaanxi Normal University
-
- GUO Zhihui
- School of Chemistry & Chemical Engineering, Shaanxi Normal University
書誌事項
- タイトル別名
-
- Preparation of Nafion-Ru(bpy)<sub>3</sub><sup>2+</sup>-Chitosan/Gold Nanoparticles Composite Film and Its Electrochemiluminescence Application
この論文をさがす
抄録
In this research, it was found that a composite film could be formed by mixing Nafion with chitosan on the graphite electrode surface. Then, based on the strong absorption of both chitosan for AuCl4− and Nafion for Ru(bpy)32+, respectively, the gold nanoparticles and electrochemiluminescence (ECL) active molecules, Ru(bpy)32+, were effectively incorporated into the composite film of chitosan with Nafion. Lastly, based on the interaction of Ru(bpy)32+ with Nafion inside the Nafion-chitosan/gold nanoparticles film, Ru(bpy)32+ was successfully immobilized within this composite film. In this case, a new composite film for fabricating Ru(bpy)32+-based ECL sensors was developed. The performances of this composite film were characterized by transmission electron microscopy (TEM), electrochemistry and electrochemiluminescence methods. Our results showed that: firstly, the gold nanoparticles in the resulting composite film could act as conducting pathways to connect Ru(bpy)32+ sites; the electrode surface accelerated the charge transport through the composite film, and the diffusion coefficient of Ru(bpy)32+ within this composite film modified electrode was 65 times higher than that of the pure Nafion film modified electrode. Secondly, due to its unique polymeric cationic character and better film-forming properties, chitosan could improve the compact structure of pure Nafion and greatly enhance the mass-transfer speed of Ru(bpy)32+. Then, the co-reactant tripropylamine (TPA) inside the composite film could offer better ECL performances such as more rapid ECL response speed, longer-term stability and higher sensitivity compared with the performances of pure Nafion film.
収録刊行物
-
- Analytical Sciences
-
Analytical Sciences 28 (6), 571-576, 2012
社団法人 日本分析化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204259971840
-
- NII論文ID
- 10030757923
-
- NII書誌ID
- AA10500785
-
- COI
- 1:STN:280:DC%2BC38jksVKjsQ%3D%3D
-
- ISSN
- 13482246
- 09106340
-
- NDL書誌ID
- 023689184
-
- PubMed
- 22729042
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- PubMed
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可