Alumina ceramics precursor was coated on the glass fibers by sol-gel method using metal alkoxide solution. The optimum coating condition for the concentration of metal alkoxide and silane coupling agent make it possible to uniformly coat alumina precursor film on the glass fiber. The organic contents in alumina precursor on the glass fiber increased with the concentration of metal alkoxide. The addition of silane coupling agent led adhesive force between glass fiber and ceramics precursor films to be higher. The alkali-resistance, heat resistance and tensile strength of ceramics precursor coating glass fibers were superior to original glass fiber. The surface of glass fiber was eroded by curing in NaOH aqueous solution at 40°C. However, the morphology of fiber coated by alumina precursor was retained in NaOH aqueous solution. The crack on the surface of glass fiber was formed by heating at 800°C, but, the crack was not observed in the glass fiber coated by alumina precursor. The tensile strength of glass fiber and alumina precursor coating fiber was 60×103and80×103kgf/cm2, respectively. The tensile stren of glass fiber and alumina precursor coating fiber increased with the concentration of silane coupling agent.
収録刊行物
-
- 繊維機械学会誌
-
繊維機械学会誌 51 (10), T199-T204, 1998
一般社団法人 日本繊維機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204266200320
-
- NII論文ID
- 130004129815
- 10002102417
-
- NII書誌ID
- AN00285892
-
- ISSN
- 18801994
- 03710580
-
- NDL書誌ID
- 4587537
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可