木材保護着色塗料で塗装した木製サッシの耐候性評価

書誌事項

タイトル別名
  • Estimation of Weather Resistance of Wooden Sashes Finished with Exterior Stains.
  • モクザイ ホゴ チャクショク トリョウ デ トソウシタ モクセイ サッシ ノ

この論文をさがす

抄録

Commercial wooden sashes and smaller wood specimens were finished with 5 kinds of exterior stains (pigmented stains) which were either of the penetrating or semi-film forming type. Finished wood was exposed outdoors and its weather resistance and the performance of the finishes were periodically evaluated by mainly their weight and dimensional changes, and color difference. Weight and dimensional changes in wood samples finishes with penetrating type stains were improved by approximately 20% and 35%, respectively. Finishing with semi-film forming type stains also improved weight changes by about 50 to 60% and dimensional changes by 55%. Exterior exposure of full-sized sashes resulted in large dimensional changes in the cross section of the longitudinal components of the frame. In finished sashes, dimensional changes in the cross section of the longitudinal components were approximately 50% smaller and dimensional changes between the various parts of the sashes were also reduced. Large color changes were observed at the upper surface of horizontal sash frames during exterior exposure and a noticeable difference in color between the horizontal and vertical frames developed over time. However, color differences between sash components was reduced as a result of finishing with exterior stains. From these results, it can be concluded that finishing is a highly effective means of improving the weather resistance of wooden sashes and that water proofing of the cross sections of longitudinal frames and careful finishing of the horizontal surfaces should be undertaken before sashes are exposed outdoors. Property enhancement produced by penetrating type stains was inferior to that of semi-film forming type stains. However, the mode of failure of penetrating type stains was superior to that of film forming type, since wood surfaces treated with the former showed gradual deterioration over time whereas the deterioration of those finished with semi-film forming type stains occurred quite suddenly. Furthermore once films degraded, property enhancement provided by the finish decreased markedly. The first maintenance interval for penetrating and semi-film forming type finishes was similar, approximately two years.

収録刊行物

被引用文献 (2)*注記

もっと見る

参考文献 (8)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ