- Simulation of Quenching Crack Generation in Low Alloy Cast Steel by Using Heat-treatment CAE Software
- ネツ ショリ CAE ソフトウェア オ カツヨウ シタ テイゴウキン チュウコウザイ ノ ヤキワレ ハッセイ シミュレーション
この論文をさがす
抄録
In order to understand the quenching crack phenomenon in cast steel, a disk shaped low alloy cast steel specimen having a opening was quenched in water at 1123K. The behavior of a quench crack was investigated by microstructure observation and analyzed by the Heat treatment CAE software. The results obtained are as follows. (1) The quench cracking easily occured as the volume of specimen increased. The mass effect for quenching crack was significant. (2) The quench cracking was due to time lag in martensitic transformation at surface side and inner side of the quenched specimen, but not due to the thermal stress in the specimen. (3) The behavior of a quenching crack was able to be predicted by the Heat treatment CAE software. (4) Therefore, the Heat treatment CAE software is useful for a counterplan preventing the quenching crack.
収録刊行物
-
- 素材物性学雑誌
-
素材物性学雑誌 17 (1), 8-12, 2004
日本素材物性学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204346951040
-
- NII論文ID
- 130003816584
- 110000952737
-
- NII書誌ID
- AN10140273
-
- ISSN
- 18846610
- 09199853
-
- HANDLE
- 10295/596
-
- NDL書誌ID
- 7109241
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可