Hot Isostatic Pressing of Submicron La2Zr2O7 Powder Prepared by the Hydrazine Method.
-
- Matsumura Y.
- Faculty of Engineering, Doshisha University
-
- Yoshinaka M.
- Faculty of Engineering, Doshisha University
-
- Hirota K.
- Faculty of Engineering, Doshisha University
-
- Yamaguchi O.
- Faculty of Engineering, Doshisha University
書誌事項
- タイトル別名
-
- Hot Isostatic Pressing of Submicron La2
この論文をさがす
抄録
In the ZrO2-La2O3 system, metastable c-ZrO2 solid solutions (ss) containing up to ≈27 mo1% La2O3 crystallize at low temperatures from amorphous materials prepared by the hydrazine method The formation of La2Zr2O7 proceeds via two reaction processes; (i) decomposition of c-ZrO2 (ss) (c-ZrO2 (ss) → La2Zr2O7 + t-ZrO2) above 1100°C and (ii) asolid-state reaction of t-ZrO2 and La2O3 at 1200° to 1300°C. Submicron La2Zr2O7 powder is producedat 1300°C. Dense La2Zr2O7 ceramics (99. 5% of theoretical) with an average grain size of 10 μm have been fabricated by hot isostatic pressing (1500°C/2h/196MPa). Their fracture toughness and bending strength are 1. 9 MPa-m1/2 and 172 MPa, respectively. They exhibit an electrical conductivity of 1. 5x10-1 S-m-1 at 1000°C.
収録刊行物
-
- 高圧力の科学と技術
-
高圧力の科学と技術 7 1063-1065, 1998
日本高圧力学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204382437888
-
- NII論文ID
- 10002692813
-
- NII書誌ID
- AN10452913
-
- ISSN
- 13481940
- 0917639X
-
- NDL書誌ID
- 4494148
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可