Polymerization Properties and Morphology in LB Films of a Long Chain Diynoic Acid as the Manganese Salt
-
- MATSUDA Hiroshi
- Canon Research Center
-
- EGUCHI Ken
- Canon Research Center
-
- NAKAGIRI Takashi
- Canon Research Center
Bibliographic Information
- Other Title
-
- 長鎖アルキルジイン酸マンガン塩LB膜の重合特性
- チョウサ アルキルジインサン マンガンエン LB マク ノ ジュウゴウ トクセ
Search this article
Abstract
The Langmuir-Blodgett (LB) multilayers of the manganese salt of 10, 12-pentacosadiynoic acid (12-8 ADA) were prepared. The polymerization behavior by UV-irradiation was similar to that of well known 12-8 ADA multilayers as the cadmium salt. But the polymerization and the phase transition from a blue form to a red form during polymerization were accelerated about 4 times and the absorption of a final polymer was twice as large compared with the cadmium salt (Fig.2). These observations indicated that the side chain was much more flexible in a LB-multilayer of 12-8 ADA as the manganese salt than the cadmium salt. From X-ray diffraction studies, changes of interlayer spacings during the polymerization process were measured. Marginal decrease was observed for the manganese salt with approximately=0.6%, but significant decrease was observed for the cadmium salt with approximately 8% (Table 1). The results indicated more favorable packing in the 12-8 ADA multilayer for the polymerization as a manganese salt and supported the smooth polymerization process. Polarizing micrographs indicated large domains of a maximum size of 3 x 1 mm and crystallographic register between layers were formed in polymeric LB-multilayers of 12-8 ADA as the manganese salt (Figs.6-8).
Journal
-
- NIPPON KAGAKU KAISHI
-
NIPPON KAGAKU KAISHI 1987 (11), 2157-2162, 1987-11-10
The Chemical Society of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204390286976
-
- NII Article ID
- 130004158560
- 40002844969
-
- NII Book ID
- AN00186595
-
- ISSN
- 21850925
- 03694577
-
- NDL BIB ID
- 3155936
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed