- Synthesis of Crystalline Mullite Fine Powders at Low Temperature by Hydrothermal Treatment of Mixed Alkoxide
- コンゴウ アルコキシド ノ スイネツ ショリ ニ ヨル ケッショウセイ ムライ
この論文をさがす
抄録
Hydrothermal conditions for the synthesis of mullite powders from mixed alkoxide containing Al2O2:SiO2=3: 2(mole ratio) were investigated at 300-600°C under 10-100 MPa for 2-168 h. Above 20 MPa, fine crystalline mullite powders were obtained at 600°C within 2 h. To produce homogeneous mullite powders, the hydrothermal treatments below 30 MPa at 600°C were preferable, because hydralsite(2Al2O2:SiO2·H2) and AS(H)-11 (5 Al2O2·2SiO2 n H2) were produced prior to mullite above 30 MPa at 600°C. In the produce prepared at 600°C under 20 MPa for 2 h, accicular particles of 100 nm in length and 20 nm in width were observed under the transmission electron microscope(TEM). The particles grew up to more than 1, um in length and 20 nm in width at 600°C under 20 MPa for 168 h. The energy dispersive spectrometry(EDS) proved that the prepared particles had the constant Al2O2/SiO2mole ratio(=3/2). The synthesized particles was revealed to be mullite by IR absoption method.
収録刊行物
-
- 日本化学会誌(化学と工業化学)
-
日本化学会誌(化学と工業化学) 1984 (6), 792-799, 1984
公益社団法人 日本化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204390326400
-
- NII論文ID
- 130004157832
- 40002843642
-
- NII書誌ID
- AN00186595
-
- ISSN
- 21850925
- 03694577
-
- NDL書誌ID
- 2984261
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可