- Simple Evaluation Method of Fracture Toughness for Si3N4 and SiC.
- チッカ ケイソ ト タンカ ケイソ ノ ハカイ ジンセイ ノ カンベン ヒョウ
この論文をさがす
抄録
A simple technique was developed to introduce fatigue precrack to a through-notched compact specimen of Si3N4 and SiC. First, a compressive load was applied to introduce damage at the notch tip. Nucleation of damage can be easily detected by a pop-in sound. Then, a fatigue crack was introduced by cyclic tensile loading. By using precracked specimens, usefulness was confirmed for fracture toughness, fatigue crack growth, and stress corrosion cracking tests. In both cases, it was found that fracture mechanics characteristics are successfully evaluated when the fatigue crack increment from the notch tip was larger than the notch tip radius.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 59 (560), 1024-1029, 1993
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204416694400
-
- NII論文ID
- 110002371490
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3825531
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可