- A study on fatigue fracture mechanisms of short fiber reinforced PET composite by the acoustic emission methed. Effects of loading direction and fiber content.
- AEホウ ニ ヨル タンセンイ キョウカ PET ノ ヒロウ ハカイ キコウ
この論文をさがす
抄録
Effects of the loading direction and the fiber content on the fatigue crack growth behavior of FRPET are studied by the acoustic emission method. From the behavior of AE event count rate, the fatigue crack growth process is divided into three zones similar to the three stages of the fatigue crack growth curve. Many AE generations under the mean load phase suggest nearness to the final fracture. Three kinds of damage modes occur at all zones in a specimen for which the angle between the directions of loading and injection is 0°(parallel), but not in the specimens of 90°(perpendicular) and 45°(oblique) angles. Fiber breakage is a dominant damage mode in all zones of the fatigue crack growth process in specimens of fiber contents of 15 and 45 % by weight.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 56 (525), 1036-1043, 1990
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204417617664
-
- NII論文ID
- 110002373088
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3661067
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可