- The Estimation of Fatigue Crack Growth Velocity from Fatigue Lifetime Distribution of Ceramics.
- セラミックス ノ ヒロウ ジュミョウ ブンプ カラ ノ キレツ シンテン ソク
この論文をさがす
抄録
A statistical method for lifetime prediction is important for determination of the fatigue behavior of ceramics, because the lifetime data of ceramic materials are scattered. In this study, the lifetime data of silicon nitride ceramics were obtained using piezo bimorph fatigue equipment with stress ratio R =0.1 and frequency f=150 Hz (sine wave) . A statistical method for estimating the relationship between the initial applied stress intensity factor (KImax) and the fatigue lifetime (Nf) was proposed. By this method, a single KImax-N<SUB>f diagram was obtained even if the maximum applied stress levels had been different in cyclic fatigue testing. It was proved that the distribution of the fatigue lifetime was determined by the distribution of initial cracks. The crack growth rate (KI-V) diagram was estimated using Fett's method from the K<Imax</SUB>-Nf diagram. Acceleration of the crack growth rate in natural cracks was observed in the region of lower applied stress intensities.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 59 (561), 1256-1261, 1993
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204418137344
-
- NII論文ID
- 110002371528
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3825507
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可