- 【Updated on May 12, 2025】 Integration of CiNii Dissertations and CiNii Books into CiNii Research
- Trial version of CiNii Research Knowledge Graph Search feature is available on CiNii Labs
- 【Updated on June 30, 2025】Suspension and deletion of data provided by Nikkei BP
- Regarding the recording of “Research Data” and “Evidence Data”
-
- MORIOKA Yoshio
- Department of Synthetic Chemistry, Faculty of Engineering, Shizuoka University
-
- AOYAMA Kazuki
- 現在ライオン油脂株式会社
-
- KASHIWADA Shigeru
- Department of Synthetic Chemistry, Faculty of Engineering, Shizuoka University
-
- KOBAYASHI Jun-ichi
- Department of Synthetic Chemistry, Faculty of Engineering, Shizuoka University
-
- HIGUCHI Izumi
- 現在沼津工業高等専門学校
Bibliographic Information
- Other Title
-
- アルミナの細孔内における液体の圧縮現象
Search this article
Description
Real density ρr (Tables 1 and 2) and sorption property (Table 3) of porous alumina and silica were measured by use of several kinds of liquid. The pore structure of each sample was diversified by calcination at different temperatures. No difference in pr was detected for silicas with different immersing liquids. But for aluminas, unless calcined at higher temperature, a large difference in ρr was observed.<BR>If this difference in pr is due to the compression of the immersing liquid, the decrease in volume by compression, ΔV, can be expressed by ΔVr=1/ρ. -1/ρ, (Table 4); where pHe is the true density measured with helium gas. A linear relationship between 417, and the volume of BET capacity m, viz. the surface area of the solid (Fig.1) demonstrates that the compres- sion of liquid in a capillary takes place on the solid surface.<BR>The total pore volume evaluated from the saturated amount of the sorption using bulk density of liquid was nearly independent of the kind of liquid used (Table 3). The value became more satisfactory when the compression effect was taken into account (Table 5). Present results imply that the compression of the adsorbed layer takes place in the measurement of sorption as well as in the measurement of density.
Journal
-
- NIPPON KAGAKU KAISHI
-
NIPPON KAGAKU KAISHI 1975 (12), 2065-2068, 1975-12-10
The Chemical Society of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204418614656
-
- NII Article ID
- 130004059614
-
- ISSN
- 21850925
- 03694577
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed