- Effects of Vickers indented load and microstructure of bending strength and fracture toughness in normal-sintered silicon carbide.
- ジョウアツ ショウケツ タンカ ケイソ ノ マゲ キョウド ト ハカイ ジンセ
この論文をさがす
抄録
Vickers hardness, four-point bending tests and fracture toughness evaluation by means of two kinds of indentation methods (ISB and IF methods) were conducted on normal-sintered silicon carbide (SiC). To investigate the microstructure on the hardness, HV, the bending strength, σf, and the fracture toughness, KIC, three kinds of SiC materials (materials A, B and C) with different sintering temperatures were prepared. Material A, of lowest sintering temperature, had the smallest grain, lower density and higher porosity. On the other hand, material C, of highest sintering temperature, had abnormal grown grains, higher density and a lower porosity which were equal to material B. The HV decreased with increasing indentation load, P, for all three materials. The indentation shapes were comparatively clear, and on the fracture surface of materials A and B, four cracks initiated from the four vertices of the indentation as clear radial and median cracks. For material C, a part of the surface peeled off due to the effect of lateral cracks on the surface layer, and the fracture surface was not flat. The σf decreased with increasing P for all three materials. The σf of material C was smaller than those of the other materials for the smooth specimens, and the variation of the σf of material C was larger than the other materials for the smooth and precracked specimens in all cases. The KIC determined by the ISB method was smaller than that by the IF method in the same P condition, and the KIC by the IF method decreased with increasing P and was saturated in the range of P ≥ 10 N.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 56 (523), 488-493, 1990
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204418778752
-
- NII論文ID
- 110002377939
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3654047
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可