球状パーライト組織を有する共析鋼の疲労強度に及ぼす微小予ひずみの影響

DOI Web Site Web Site

書誌事項

タイトル別名
  • Effects of small prestrain on fatigue strength of eutectoid steel with spheroidal pearlite structure.
  • キュウジョウ パーライト ソシキ オ ユウスル キョウセキ コウ ノ ヒロウ

この論文をさがす

抄録

In order to clarify the effect of small prestrain on the fatigue strength of carbon steel, fatigue behavior of plain specimens of eutectoid steel subjected to tensile prestrains is investigated, and compared with that of annealed or strain-aged specimens. It is found that small prestrain of a few percent does not decrease either the fatigue limit or the crack initiation and propagation lives. Fatigue slip initiation, however, is accelerated by the small prestrain. It is also found that no cyclic strain aging occurs. From these results, it is concluded that dislocations are unpinned by the small prestrain and this causes fatigue slip to occur easily, but the fatigue behavior after the slip initiation is not affected because spheroidal cementite acts as obstacles to further slip deformation and the stage I crack propagation.

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ