- Stable Crack Growth of Surface Crack across the Fusion Line. 2nd Report. Analysis of Q-Factor.
- ヨウセツブ ニ ソンザイスル ヒョウメン キレツ ノ アンテイ セイチョウ シ
この論文をさがす
抄録
Stable crack growth tests are conducted using CT specimens and surface-cracked specimens welded of A533B steel and HT80 steel. The distribution patterns of SZW and Δa values along the crack front are measured, and the effects of welding and fusion line are considered. The results show that the effects of fusion line appear clearly in Δa distribution along the crack front. Δa is much larger in HT80 steel than in A533B steel. Three dimensional finite element analyses are then conducted. The J-integral distribution along the crack front is obtained and the crack tip fields are compared with HRR (Huthcinson, Rice and Rosengren) solutions. The Q-factor is also evaluated along the three-dimensional crack front. It is found that the Q-factor controls the local crack growth behavior near the fusion line.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 60 (569), 31-36, 1994
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204446626304
-
- NII論文ID
- 110002372123
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3859473
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可