- Investigation of Threshold Stress Intensity Factor and Plastic Deformation of Crack Tip for Hydrogen-Assisted Cracking of 2.25Cr-1Mo Steel.
- 2.25Cr 1Mo コウ ノ スイソ ジョチョウ ワレ カゲンカイ オウリョ
この論文をさがす
抄録
For hydrogen-assisted cracking of 2.25 Cr-1 Mo steel, the evaluation of the threshold stress intensity factor for subcritical crack growth was examined by employing the slow strain rate test. Also, by the method of recrystallization, a high strain region formed at the crack tip was observed, and the effect of hydrogen on plastic deformation was studied. By this experiment, it was shown that hydrogen promoted subcritical crack growth at a low stress intensity level, KIH(40∼80 MPa·m1/2)well below KIc(300∼400 MP·m1/2, and hydrogen also enhanced plastic deformation at the crack tip. This result suggests that the plastic deformation which is enhanced by hydrogen exerts large effects on subcritical crack growth in hydrogen-assisted cracking of 2.25 Cr-1 Mo steel.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 61 (582), 283-288, 1995
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204447277568
-
- NII論文ID
- 110002372236
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3601618
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可