- Fatigue Strength of Low-Carbon High-Manganese Steels and Their Fatigue Crack Initiation.
- テイ タンソ コウ マンガン コウ ノ ヒロウ キョウド ヒョウカ
この論文をさがす
抄録
Rotating bending fatigue tests had been performed to investigate the effect of carbon content on the characteristics of fatigue crack initiation, using four kinds of high-manganese steels with carbon content between 0.025%-0.10%. Although there exist nonpropagating cracks in HM steel (0.178% carbon) under the fatigue limit of l07 cycles, these cracks are not observed in four kinds of HM steels (0.025-0.1% carbon) under the stress of each fatigue limit by l07 cycles. From this, the limit of existence for nonpropagating cracks is concluded to be between 0.1%∼0.2% of carbon content, and the characteristics for crack initiation under the fatigue limit of l07 cycles are founded to be prodominantly influenced by the carbon content.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 61 (582), 239-244, 1995
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204447290752
-
- NII論文ID
- 110002372229
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3601670
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可