- Evaluation of Sphere Indentation Damage and Residual Strength in Ceramics. SiC Sphere Indentation to SiC Specimen-Case of Elastic Condition.
- セラミックス ノ ショウ キュウ オシコミ ソンショウ ト ザンリュウ キョウ
この論文をさがす
抄録
A silicon carbide sphere indentation was subjected to the surface of silicon carbide plate specimen to examine indentation damage patterns and residual strength of the specimen. After the residual strength of the damaged specimen was measured by the four-point flexural test, damage patterns were observed with the scanning electron microscope. In the case that the cone crack (equivalent to elastic damage) was the fracture origin, the residual strength was evaluated. A method of approximate analysis of cone crack taking account of mechanism of stable crack growth was proposed. The estimated values were almost in agreement with the measured values.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 64 (619), 675-680, 1998
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204447309056
-
- NII論文ID
- 110002374483
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DyaK1cXjtl2is78%3D
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- NDL書誌ID
- 4434620
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可