- Evaluation of Surface Damage and Residual Strength in Ceramics due to Sphere Impact. 3rd Report, SiC Sphere Impact to SiC Specimen.
- ショウ キュウ ショウトツ ソンショウ ニ ヨル セラミックス ノ キョウド テイカ ニ カンスル ケンキュウ 3 タンカ ケイソ ヘイバン エ ノ タンカ ケイソ キュウ ショウトツ
この論文をさがす
抄録
In order to elucidate mechanisms of surface damage and to establish methods for evaluating strength degradation in ceramics subjected to dynamic contact with solid particles, silicon carbide sphere impact tests were carried out for silicon carbide specimens. A gas-gun-type apparatus was used for these tests. The residual strengths of the surface damaged specimens were measured by flexural tests. Damage analysis and residual strength evaluation were conducted. For the case of elastic damage (cone crack), the residual strength could be evaluated using indentation analysis, up to low speed range, in which the specimen was not ruptured by impact.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 65 (634), 1276-1281, 1999
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204447421952
-
- NII論文ID
- 110002375016
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 4776607
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可