- Improvement of High Cycle Fatigue Strength by Hot Isostatic Pressing on Ferritic Ductile Cast Iron.
- HIP ショリ ニヨル FDIザイ ノ コウ サイクル ヒロウ キョウド ノ
この論文をさがす
抄録
Cast defects such as microshrinkage reduce the for fatigue strength and reliabilty of ductile cast iron even though full attention is given for production of the test piece, and so HIP (hot isostatic pressing) is applied to FDI (ferritic ductile cast iron) in order to reduce microshrinkage. After that, rotating bending fatigue tests were carried out. HIP did not change the properties of graphite drains such as mean diameter, nodularity and nodule count. However microshrinkage in the HIP-FDI was completely suppressed. The reduction effect of cast defects by HIP treatment was shown by density measurement and the mesults of close observations of the fracture surface and the crack initiation site. The fatigue strength was improved at the whole region of fatigue life and the fatigue limit was about 1.32 times that of the material subjected to heat treatment with HIP.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 62 (604), 2681-2686, 1996
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204448380672
-
- NII論文ID
- 110002372954
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 4104504
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可