- Study on Weld Characteristics of Thin-wall Injection Molded Polypropylene Plates
- ポリプロピレン ウスニク シャシュツ セイケイヒン ノ ウェルド ニ カンスル ケンキュウ
この論文をさがす
説明
This paper deals with a fundamental study on the weld structure of thin-wall injection molded polypropylene plates. Effects of the mold temperature and plate thickness on the weld characteristics were investigated. In the experiment, several measurements were performed; distribution of the optical retardation, specific latent heat for fusion, V notch depth and width, and tensile strength of the specimen. The results indicated that the fountain flow of the melt occurred in the filling stage even with a plate thickness of 0.3 mm. It was also shown that molecular orientation in the weld region was relatively low. Thermal property measurement showed that crystallinity of the molded specimen was affected not only by the mold wall temperature but also by the plate thickness. Mechanical strength reduction by the existence of the weld was experimentally confirmed through the tensile test, and it was shown that the thin-wall polypropylene plate molded at high mold temperature broke from the weld region under small strain.
収録刊行物
-
- 成形加工
-
成形加工 20 (10), 776-780, 2008
一般社団法人 プラスチック成形加工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204460727680
-
- NII論文ID
- 10023961100
-
- NII書誌ID
- AN10278882
-
- ISSN
- 18837417
- 09154027
-
- NDL書誌ID
- 9666654
-
- 本文言語コード
- ja
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可