- Study on Combustion Behavior of PBT Polymer in Injection Molding by Combustion Gas Collection and Component Analysis
- ミノル セイケイジ ノ ネンショウ ガス シュウシュウ ト ガス ソセイ ブンセキ ニ ヨル PBT ネンショウ キョドウ ニ カンスル ケンキュウ
この論文をさがす
説明
Burn marks are serious defects that can occur during injection molding, and from the viewpoint of the molding engineer, are a problem that urgently needs to be solved. In the present study, a gas collection and component analysis system was used to determine the gas production mechanism during injection molding of PBT polymer. The relationship between the occurrence of burn marks, the injection speed and the gas production mechanism was investigated, and the following results were obtained.<br>1) The principal components in the collected gas were CO2, CO, CH4 and H2.<br>2) When burn marks were observed, about 70% of the collected gas was CO2.<br>3) It is thought that there are some important chemical reactions occur during the plastic molding process.<br>4) According to the characteristic of chemical reactions, it is inferred that the parts of metal in injection machine and mold have important effects on chemical reactions.<br>5) When the injection speed was higher, the chemical reaction that is related to the methanation was retarded.
収録刊行物
-
- 成形加工
-
成形加工 26 (1), 27-33, 2014
一般社団法人 プラスチック成形加工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204462810240
-
- NII論文ID
- 130006646943
-
- NII書誌ID
- AN10278882
-
- ISSN
- 18837417
- 09154027
-
- NDL書誌ID
- 025127951
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可